HDPE Geomembrane is made of finest quality high density polyethylene (HDPE) with specially formulated, virgin polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which makes our smooth geomembrane HDPE Geomembrane with excellent resistance to UV radiation and is suitable for exposed conditions.
Product Parameters
| Item | Test Value | ||||||
| 0.30 mm | 0.5 mm | 0.75 mm | 1.0 mm | 1.5 mm | 2.0 mm | 3.0 mm | |
| Minimum Density(g/cm³) | 0.94 | ||||||
| Strength at yield,N/mm | 5 | 8 | 11 | 15 | 22 | 29 | 44 |
| Strength at break ,N/mm | 8 | 14 | 20 | 28 | 40 | 53 | 80 |
| Elongation at yield,% | 13 | ||||||
| Elongation at break,% | 720min | ||||||
| Tear Resistance N | 40 | 65 | 93 | 125 | 190 | 250 | 375 |
| Puncture Resistance N | 105 | 176 | 240 | 320 | 480 | 640 | 960 |
| Stress Crack Resistance, hrs | 300 | ||||||
| Carbon Black Content, % | 2.0-3.0 | ||||||
| Carbon Black Dispersion | 1 or 2 | ||||||
| Standard OIT Min | 100 | ||||||
| High Pressure OIT Min | 400 | ||||||
| 85ºC Heat aging(OIT Retention rate at Normal pressure after 90d ) % | 85 | ||||||
| UV resistance (OIT retention rate after 1600 hours of UV radiation) | 65 | ||||||
| Impact Cold Crack at -70°C | Pass | ||||||
| Water vapor permeability (g.cm/cm2 .s.Pa) | ≤1.0×10-13 | ||||||
| Dimensional Stability (%) | ±2 | ||||||
Production Flow
Application
14.Traffic facilities
HDPE Geomembrane is made of finest quality high density polyethylene (HDPE) with specially formulated, virgin polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which makes our smooth geomembrane HDPE Geomembrane with excellent resistance to UV radiation and is suitable for exposed conditions.
Product Parameters
| Item | Test Value | ||||||
| 0.30 mm | 0.5 mm | 0.75 mm | 1.0 mm | 1.5 mm | 2.0 mm | 3.0 mm | |
| Minimum Density(g/cm³) | 0.94 | ||||||
| Strength at yield,N/mm | 5 | 8 | 11 | 15 | 22 | 29 | 44 |
| Strength at break ,N/mm | 8 | 14 | 20 | 28 | 40 | 53 | 80 |
| Elongation at yield,% | 13 | ||||||
| Elongation at break,% | 720min | ||||||
| Tear Resistance N | 40 | 65 | 93 | 125 | 190 | 250 | 375 |
| Puncture Resistance N | 105 | 176 | 240 | 320 | 480 | 640 | 960 |
| Stress Crack Resistance, hrs | 300 | ||||||
| Carbon Black Content, % | 2.0-3.0 | ||||||
| Carbon Black Dispersion | 1 or 2 | ||||||
| Standard OIT Min | 100 | ||||||
| High Pressure OIT Min | 400 | ||||||
| 85ºC Heat aging(OIT Retention rate at Normal pressure after 90d ) % | 85 | ||||||
| UV resistance (OIT retention rate after 1600 hours of UV radiation) | 65 | ||||||
| Impact Cold Crack at -70°C | Pass | ||||||
| Water vapor permeability (g.cm/cm2 .s.Pa) | ≤1.0×10-13 | ||||||
| Dimensional Stability (%) | ±2 | ||||||